Pala, KanşadTekçe, NeslihanTuncer, SafaDemirci, Mustafaöznurhan, FatihSerim, Merve2024-10-262024-10-2620171989-5488https://doi.org/10.4317/jced.53463https://hdl.handle.net/20.500.12418/26676Background: This study aimed to evaluate the flexural strength and microhardness of three different anterior composites after 10 000 thermocycles. Material and Methods: The mechanical properties of a nano-fill composite (Filtek Ultimate Universal Restorative (FUR) (Enamel)), a nano-hybrid composite (Clearfil Majesty ES2 (ES2) (Enamel)), and a micro-hybrid composite (G Aenial Anterior (GAA)) were investigated in this study. For the microhardness test, 8-mm diameter and 2-mm thickness composite discs were used (n = 10), and for the flexural strength test, 25x2x2 mm bar-shaped specimens were prepared (n = 13). The specimens were tested at 24 h and after 10 000 thermocycles. Data were analyzed using two-way analysis of variance and the post-hoc Tukey test (p < .05). Correlations between hardness and flexural strength were calculated using Pearson's correlation analysis. Results: There was a significant difference in the microhardness values of the materials (p < .05). FUR exhibited significantly higher microhardness than ES2 and GAA. However, the flexural strength of three composites was statistically similar at 24 h (p > .05). Pearson correlation analysis revealed that there was a negative relationship between the mean hardness and flexural strength values (correlation coefficient = -0.367, p = .043). After 10 000 thermocycles, microhardness values of each material and flexural strength of ES2 and GAA decreased significantly according to 24 h. Conclusions: The nano-fill composite FUR displayed significantly higher microhardness values. However, each resin composite was statistically similar for flexural strength values. Ten thousand thermocycles significantly affected microhardness and flexural strength. © Medicina Oral S. L. C.I.F. B 96689336.en10.4317/jced.53463info:eu-repo/semantics/openAccessAnterior composites; Flexural strength; MicrohardnessArticle93e430e4242-s2.0-85014866468Q2