The effects of thermomechanical processing on the grain size, tensile strength, and strain rate of a CuZn10 alloy were investigated. Microstructures of thermomechanically treated samples were introduced using a scanning ...

In the present study, cementation steel was exposed to boronizing process at 950 °C for 6, 8, and 10 h. Microstructural changes on the surface of the samples after boron operation were inspected by optical microscope, ...

In this study, AISI 304 stainless steel and DUROSTAT 500 steel are combined using TIG double-sided arc welding. Microstructural differences of welded joints were researched by using a scanning electron microscope (SEM), ...

FeTi-FeB was added to molten high chromium white cast iron in amounts of 0.5–2.5 wt% at 50 °C above the melting temperature. The samples were produced in four groups. The first group samples were investigated as cast, the ...

A new AlCrFeSrTiBSi master alloy was manufactured by in situ synthesis in Al melt, and compared with AlBSr master alloy. Microstructures of A356 alloy modified with AlCrFeSrTiBSi master alloy were investigated, and the ...

AISI 1040 and AISI 304 steel plates of 10 mm were joined without pretreatment by double-sided TIG arc welding (DSAW). Joints were manufactured by using welding currents of 420, 440, and 460 A. The microstructural variations ...