dc.description.abstract | This paper reports the temperature effects on the optical properties of metalorganic vapour-phase epitaxy
(MOCVD) grown c-axis oriented AlN epilayer thin film studied by in-situ high-temperature spectroscopic
ellipsometry. The crystal structure and the quality of the grown AlN epilayer film are analyzed using X-ray
Diffraction and rocking curve techniques, respectively. Modelling of the ellipsometric data revealed that the
uniaxial anisotropic refractive indices of the c-axis oriented film in the directions n‖ and n⊥ increased from 2.50
to 2.59 and 2.32 to 2.37, respectively with the increase in temperature from 223 to 573 K. The thermo-optic
coefficients were evaluated to be around 10− 5
. Nano-mechanical characterization of this film showed an
average hardness of 19.4 GPa at ambient temperature, which is higher than a-axis oriented AlN film. The average
surface free energy of the synthesized film as evaluated from contact angle measurements is reported to be
around 36.22 ± 0.64 mN/m. These results are highly relevant for a better understanding of c-axis oriented AlNbased materials in high-temperature ultraviolet optical devices. | tr |
dc.rights | info:eu-repo/semantics/closedAccess | tr |
dc.title | Optical and nano-mechanical characterization of c-axis oriented AlN film | tr |
dc.type | article | tr |
dc.contributor.department | Mühendislik Fakültesi | tr |
dc.relation.publicationcategory | Rapor | tr |