Now showing items 21-30 of 41
Effect of Austempering Treatment on Metallurgical Structure of Ce Inoculated X210Cr12 Cold Work Tool Steel
(http://www.degruyter.com, 21 Februar)
The effect of austempering treatment on metallurgical structure of X210Cr12 cold work tool steel inoculated with Ce was researched. Microstructural changes, elemental characterizations, and phase formations of the samples ...
Investigation of Surface Properties and FeB-Fe2B Layer Formation in Pack Boronizing of Cementation Steel
(World Scientific Publishing Co. Pte. Ltd., 01 Septemb)
In this study, cementation steel was boronized at 1050∘C for 6h, 8h, and 10h. Microstructural change on the surface of the samples after boronization was detected by optical microscope (OM), scanning electron microscope ...
Microstructure and Fatique Performance of Cu Based M7C3 Reinforced Composites
(http://www.degruyter.com, 09 March 2)
Cu\Fe–Cr–C metal matrix composites (MMCs) were produced with a reinforcer addition of 6, 9, 12, 15, and 18 wt% Fe–Cr–C by powder metallurgy. The effects of sintering temperatures on Cu-based Fe–Cr–C-reinforced composites ...
Effect of Thermomechanical Process on Mechanical Properties of CuZn10 Alloy
(http://www.degruyter.com, 07 July 20)
The effects of thermomechanical processing on the grain size, tensile strength, and strain rate of a CuZn10 alloy were investigated. Microstructures of thermomechanically treated samples were introduced using a scanning ...
Metallurgical Properties of Borid Layers Formed in Pack Boronized Cementation Steel
(http://www.degruyter.com, 06 Septemb)
In the present study, cementation steel was exposed to boronizing process at 950 °C for 6, 8, and 10 h. Microstructural changes on the surface of the samples after boron operation were inspected by optical microscope, ...
Microstructure and Mechanical Characteristics of AISI 304 / DUROSTAT 500 Steel Double-Side TIG Welds
(http://www.degruyter.com, 05 August )
In this study, AISI 304 stainless steel and DUROSTAT 500 steel are combined using TIG double-sided arc welding. Microstructural differences of welded joints were researched by using a scanning electron microscope (SEM), ...
Effect of FeTi-FeB Inoculation on Shape of Carbide Reinforcements in Hypoeutectic High Chromium White Cast Irons
(http://www.degruyter.com, 16 March 2)
FeTi-FeB was added to molten high chromium white cast iron in amounts of 0.5–2.5 wt% at 50 °C above the melting temperature. The samples were produced in four groups. The first group samples were investigated as cast, the ...
Effect of Ni on microstructure and wear behaviour of 13Cr-W-Mo-2C white cast iron
(CONSEJO SUPERIOR INVESTIGACIONES CIENTIFICAS-CSICEditorial CSIC, C/VITRUVIO 8, 28006 MADRID, SPAIN, 30 June 20)
The effect of Ni concentration on the microstructure and wear performance of 13Cr-(0.5-7.0) Ni-W-Mo-Mn-2C white cast iron subjected to homogenization heat treatment was examined. Concentration of Ni was altered in the range ...
Analysis of thorium and transuranium utilization in a small modular reactor
(Eylül 2022)
This study presents neutronic analyses of a small modular reactor utilizing transuranium and thorium. Two different fuel cases are considered in the analyses as the transuranium extracted from PWR-MOX spent fuel (a form ...
Analysis of reusability of ThO2 and spent UO2 fuels enriched with ads in a CANDU reactor
(Aralık 202)
The study presents the analysis of the reusability of ThO2 and spent UO2 fuels enriched in two different ADS reactors fuelled with Minor Actinide. The spent UO2 fuels are taken out from pressurized water reactor and CANDU ...